Portland Cement CEM I 42.5 R Standard TS EN 197-1:2002

CEM I 42,5 R

Product
Portland Cement

Standard
TS EN 197-1:2002 CEM I 42.5 R

Product Description
Portland cement is the product, produced by grinding clinker manufactured by burning raw materials like limestone, marl, clay, iron ore, pyrite ash, bauxite etc. at appropriate proportions by addition of a certain amount of retarder (generally gypsum) and sets and gains strength after a certain time being mixed with water.

It is generally used in works requiring high strength values, concrete works performed at low temperatures, precast buildings, tunnel-form applications, building chemical maunfacturing and foundations.

Physical Properties

	Cement	Standard	Unit
Initial Setting Time	173	min. 60	Minute
Final Setting Time	211	-	Minute
Specific Gravity	3.13	-	g/cm3
Soundness	1	max. 10	cm
Specific Surface (Blaine)	3457	-	cm2/g
Bulk Density	1008	-	g/l
2 Days Strength	27.9	min. 20	MPa
28 Days Strength	60.5	min./max. 42.5/62.5	MPa

Chemical Properties

	Cement	Standard	Unit
SO3	2.30	max. 4	%
MgO	1.05	-	%
Loss on Ignition	2.46	max. 5	%
Insoluble Residue	0.60	max. 5	%
Cl-	0.01	max. 0.1	%
Alkali Equivalent Na2O + 0.658 K2O	0.61	-	%
Free Lime	1.19	-	%

Delivery 
Sold in bulk or in 50 kg. kraft bags.

Quality Control 
Our product is certified by Council for Quality and Environment (K.Ç.K.) according to TS EN 197-1:2002 to use CE marking in Europe.

52,5 R Cement ( CEM I 52,5 R ) (cement - rebar - steel)

CEM I 52.5R

Product Portland Pozzolana Cement Standard EN 197-1 : 2000 Product Description Portland cement is a hydraulic binder that reacts with water, produced clinker and natural gypsum as retarder. Using Area Generally used in works requiring high strength values , dam and tunnel works,precast building,concrete works in low temperatures, and building chemicals manufacturing. Chemical Properties 52,5 R Cement Decleration Standard Unit SiO2 20,09 % Fe2O3 3,87 % Al2O3 4,84 % CaO 64,02 % MgO 1,15 Max 5,0 % SO3 2,83 Max 4,0 % Loss On Ignition 2,36 Max 5,0 % Insoluble Residue 0,34 Max 5,0 % Free Lime 0,80 % Alkali Equivalent (Na2O type) 0,65 % Total Additive 3,85 % Physical Properties 52,5 R Cement Decleration Standard Unit Setting Time (Initial) 165 Min 45 % Setting Time (Final) 275 - % Spesific Gravity 3,156 - % Expansion 1,00 Max 10 % Strenght for 2 days 31,10 Min 30 % Strenght for 28 days 56,40 Min 52,5 %

MUSA YAPI DIS TIC.

www.musayapi.com.tr

export@musayapi.com.tr

musayapi@musayapi.com.tr

musayapi@gmail.com

Blast Furnace Slagt Cement,CEM III/B(S) 42,5N

Blast Furnace Slagt Cement,CEM III/B(S) 42,5N

Granulated Blast Furnace Slag

Granulated Blast Furnace Slag (GBFS) is one of the waste material groups obtained from various metallurgy plants. In production of raw iron, blast furnace slag remains above raw iron due to having less weight and iron ore gangue is composed at a temperature between 1,400 to 1,600 °C after burning of coke and limestone. It is used as an additive component in ready-mix concrete, in production of type CEM III Slag cement or other types of blended cement. It is produced in conformity with the standard TS EN 15167-1.

Blast Furnace Slagt Cement,CEM III/B(S) 42,5N

CEM III B(S) 42,5 N

PRODUCT TECHNİCAL DATA FORM Name Blast Furnace Slagt Cement,CEM III/B(S) 42,5N STANDARD TS EN 197/1 CONTACT INFORMATİON DEFİNİTİON CEM III/B (S) 42,5 N type cement is a hyroulic binder which is produced by grinding 20-34 % portland clinker with 66-80 % slag and some amount of setting time regulator (gypsum). USAGE AREAS Seashore and Port Constructions ,Open Sea Constructions ,Seawage Treatment Plants, Bored Piles,Dams ,Underground,water pipes ,Industrial Zones exposed to sulphate attack, Buildings.Mass Concretes with low hydration heat. PHYSİCAL AND MECHANİCAL PROPERTİES Property Unit Standard  CEM III B (S)Cement Comperssive Strength 2 Days MPa min. 10,0 14,0 28 Days MPa 42,5-62,5 45,0 Setting Time minute min.60 180 Expansion mm max.10,0 1,0 Specific Surface cm/gr - 5200 CHEMİCAL PROPERTİES Additive Slag % 66-80 67 Comperssive Strength % max. 4,00 2,30 SO3 % max. 01000 0,0100 Chloride % max 5,00 2,00 Loss On Ignition % max 5,00 1,00 Insoluble Residue HANDLİNG Bulk.Big.Bag QUALITY CONTROL Our Product is under control of KCK(Council for Quality and Environment) and certified with CE Mark.

MUSA YAPI DIS TIC.

www.musayapi.com.tr

export@musayapi.com.tr

musayapi@musayapi.com.tr

musayapi@gmail.com