Blast Furnace Slagt Cement,CEM III/B(S) 42,5N
Granulated Blast Furnace Slag
Granulated Blast Furnace Slag (GBFS) is one of the waste material groups obtained from various metallurgy plants. In production of raw iron, blast furnace slag remains above raw iron due to having less weight and iron ore gangue is composed at a temperature between 1,400 to 1,600 °C after burning of coke and limestone. It is used as an additive component in ready-mix concrete, in production of type CEM III Slag cement or other types of blended cement. It is produced in conformity with the standard TS EN 15167-1.
Blast Furnace Slagt Cement,CEM III/B(S) 42,5N
CEM III B(S) 42,5 N
|
|
|
|
PRODUCT TECHNİCAL DATA FORM
|
Name |
Blast Furnace Slagt Cement,CEM III/B(S) 42,5N
|
|
STANDARD
|
TS EN 197/1
|
|
CONTACT INFORMATİON | |
|
|
DEFİNİTİON |
CEM III/B (S) 42,5 N type cement is a hyroulic binder
which is produced by grinding 20-34 % portland clinker with 66-80 % slag and some amount of setting time regulator (gypsum).
|
|
USAGE AREAS |
Seashore and Port Constructions ,Open Sea Constructions ,Seawage Treatment Plants, Bored Piles,Dams ,Underground,water pipes ,Industrial Zones exposed to sulphate attack, Buildings.Mass Concretes with low hydration heat.
|
|
PHYSİCAL AND MECHANİCAL PROPERTİES | Property | Unit | Standard | CEM III B (S)Cement |
Comperssive Strength | 2 Days | MPa | min. 10,0 | 14,0 |
28 Days | MPa | 42,5-62,5 | 45,0 |
Setting Time | minute | min.60 | 180 |
Expansion | mm | max.10,0 | 1,0 |
Specific Surface | cm/gr | - | 5200 |
|
CHEMİCAL PROPERTİES | Additive | Slag | % | 66-80 | 67 |
Comperssive Strength | % | max. 4,00 | 2,30 |
SO3 | % | max. 01000 | 0,0100 |
Chloride | % | max 5,00 | 2,00 |
Loss On Ignition | % | max 5,00 | 1,00 |
Insoluble Residue |
|
HANDLİNG | Bulk.Big.Bag |
|
QUALITY CONTROL |
Our Product is under control of KCK(Council for Quality and Environment) and certified with CE Mark.
|
|